Basic Info.
Conductor Material
Aluminum Clad Steel
Range of Application
Overhead Line
Certification
ISO9001, CCC
Transport Package
Wood Drum or Steel- Wood Drum
Specification
SGS ISO9001
Product Description
Aluminium Clad Steel wire ACS 7wire 6AWGStructure:The conductor is composed by bare hard-drawn, round, aluminum clad steel wires of 14% to 40% IACS conductivity
Application:It is widely used in aerial electricity transmission,overhead ground conductor, extra high voltage overhead conductor, optical fiber composite overhead ground line and self-danping conductor line,etc
Standard:ASTM B416-98, AS1222, IEC61089
Features:
ACS conductors are similar to conventional ACSR with some very important additional advantages. ACS can operate continuously at high temperatures up to 250C without damage, allowing for a significant increase in conductor current-carrying capacity. ACSS sags less under emergency electrical loadings than ACSR, it is self-damping, and its final sags are not affected by long-term creep of the aluminum.
(1)improved conductivity
(2)better self-damping property
(3)very low sag at high temperature
(4)high current carrying capacity
(5)excellent immunity to vibration fatigue
(6)long term creep of aluminum does not affect final sag
Huatong Cable Inc.
(1),More than 30 years experience.
(2) ,100,000m² factory,200 staffs,annual output 100,000 metic tons.
(3),Sound Quality Control
--Material inspection;
--manufacturing inspection;
-- Finished products inspection;
-- Inspection before delivery.
--Third party inspection.
-- Inspection of storage at port of departure.
(4),ISO Certificated.
(5) ,Plenty of material and lobor gurantee the delivery prompt and price competitive.
(6),24/7 service.
IF YOUR HAVE ANY INTERESTED PRODUCTS, PLS FEEL FREE TO CONTACT OUR SALES TEAM.
Approximate Properties of Hard-drawn 20.3% Conductivity Aluminum-Clad steel Wire (20.3%) |
|
|
Nominal Dia | Size | Calculated crosssectional area | Min tensile strength | Calculated breaking load | Mincoating thickness | D.C resistance at 20ºC≤ | Weight |
|
|
|
in. | mm | AWG | mm2 | cmils | Mpa | psi | kn | mm | Ω/1000ft | Ω/km | kg/km | 1b/1000ft |
0.2043 | 5.189 | 4 | 21.150 | 41740 | 1070 | 155000 | 22.60 | 0.259 | 1.222 | 4.009 | 139.32 | 93.63 |
0.1880 | 4.775 | 4 | 17.908 | 35342 | 1100 | 160000 | 19.70 | 0.239 | 1.443 | 4.735 | 118.01 | 79.31 |
0.1819 | 4.620 | 5 | 16.767 | 33090 | 1140 | 165000 | 18.10 | 0.231 | 1.541 | 5.056 | 110.48 | 74.25 |
0.1729 | 4.392 | 5 | 15.150 | 29899 | 1170 | 170000 | 17.73 | 0.220 | 1.706 | 5.597 | 99.84 | 67.10 |
0.1620 | 4.115 | 6 | 13.296 | 26240 | 1210 | 175000 | 16.00 | 0.206 | 1.943 | 6.375 | 87.61 | 58.88 |
0.1549 | 3.934 | 6 | 12.155 | 23989 | 1240 | 180000 | 15.07 | 0.197 | 2.126 | 6.976 | 80.10 | 53.83 |
0.1443 | 3,665 | 7 | 10.549 | 20820 | 1280 | 185000 | 13.50 | 0.183 | 2.450 | 8.038 | 69.47 | 46.69 |
0.1369 | 3.477 | 7 | 9.495 | 18739 | 1310 | 190000 | 12.44 | 0.174 | 2.722 | 8.931 | 62.57 | 42.05 |
0.1285 | 3.264 | 8 | 8.366 | 16510 | 1340 | 195000 | 11.20 | 0.163 | 3.089 | 10.135 | 55.15 | 37.03 |
0.1144 | 2.906 | 9 | 6.633 | 13090 | 1340 | 195000 | 8.92 | 0.145 | 3.896 | 12.783 | 43.70 | 29.37 |
0.1019 | 2.588 | 10 | 5.260 | 10380 | 1340 | 195000 | 7.07 | 0.129 | 4.912 | 16.116 | 34.66 | 23.29 |
0.0907 | 2.304 | 11 | 4.170 | 8230 | 1340 | 195000 | 5.61 | 0.115 | 6.194 | 20.323 | 27.48 | 18.47 |
0.0808 | 2.052 | 12 | 3.309 | 6530 | 1340 | 195000 | 4.45 | 0.103 | 7.811 | 25.628 | 21.80 | 14.65 |
Approximate Properties of Hard-drawn 27% Conductivity Aluminum-Clad steel Wire (27%) |
|
|
Nominal Dia | Size | Calculated cross sectional area | Min tensile strength | Calculated breaking load | Mincoating thickness | D.C resistance at 20ºC≤ | Weight |
|
|
|
in. | mm | AWG | mm2 | cmils | Mpa | psi | kn | mm | Ω/1000ft | Ω/km | kg/km | 1b/1000ft |
0.2043 | 5.189 | 4 | 21.150 | 41740 | 862 | 125000 | 18.20 | 0.363 | 0.920 | 3.019 | 124.99 | 84.00 |
0.1880 | 4.775 | 4 | 17.908 | 35342 | 889 | 129000 | 15.92 | 0.334 | 1.087 | 3.566 | 105.83 | 71.12 |
0.1819 | 4.620 | 5 | 16.767 | 33090 | 917 | 133000 | 15.40 | 0.323 | 1.161 | 3.809 | 99.09 | 66.59 |
0.1729 | 4.392 | 5 | 15.150 | 29899 | 945 | 137000 | 14.32 | 0.307 | 1.285 | 4.215 | 89.54 | 60.17 |
0.1620 | 4.115 | 6 | 13.296 | 26240 | 972 | 141000 | 12.90 | 0.288 | 1.464 | 4.803 | 78.57 | 52.80 |
0.1549 | 3.934 | 6 | 12.155 | 23989 | 1000 | 145000 | 12.16 | 0.275 | 1.601 | 5.254 | 71.84 | 48.28 |
0.1443 | 3,665 | 7 | 10.549 | 20820 | 1034 | 150000 | 10.90 | 0.257 | 1.845 | 6.053 | 62.33 | 41.89 |
0.1369 | 3.477 | 7 | 9.495 | 18739 | 1062 | 154000 | 10.08 | 0.243 | 2.050 | 6.726 | 56.12 | 37.71 |
0.1285 | 3.264 | 8 | 8.366 | 16510 | 1076 | 156000 | 9.00 | 0.228 | 2.326 | 7.632 | 49.43 | 33.22 |
0.1144 | 2.906 | 9 | 6.633 | 13090 | 1076 | 156000 | 7.13 | 0.203 | 2.934 | 9.626 | 39.19 | 26.34 |
0.1019 | 2.588 | 10 | 5.260 | 10380 | 1076 | 156000 | 5.66 | 0.181 | 3.700 | 12.140 | 31.08 | 20.89 |
0.0907 | 2.304 | 11 | 4.170 | 8230 | 1076 | 156000 | 4.48 | 0.161 | 4.667 | 15.312 | 24.63 | 16.55 |
0.0808 | 2.052 | 12 | 3.309 | 6530 | 1076 | 156000 | 3.56 | 0.144 | 5.882 | 19.299 | 19.55 | 13.14 |
Approximate Properties of Hard-drawn 30% Conductivity Aluminum-Clad steel Wire (30%) |
|
|
Nominal Dia | Size | Calculated cross sectional area | Min tensile strength | Calculated breaking load | Mincoating thickness | D.C resistance at 20ºC≤ | Weight |
|
|
|
in. | mm | AWG | mm2 | cmils | Mpa | psi | kn | mm | Ω/1000ft | Ω/km | kg/km | 1b/1000ft |
0.2043 | 5.189 | 4 | 21.150 | 41740 | 703 | 102000 | 14.90 | 0.389 | 0.828 | 2.717 | 118.64 | 79.73 |
0.1880 | 4.775 | 4 | 17.908 | 35342 | 731 | 106000 | 13.09 | 0.358 | 0.978 | 3.209 | 100.46 | 67.51 |
0.1819 | 4.620 | 5 | 16.767 | 33090 | 758 | 110000 | 12.70 | 0.347 | 1.045 | 3.429 | 94.06 | 63.21 |
0.1729 | 4.392 | 5 | 15.150 | 29899 | 786 | 114000 | 11.91 | 0.329 | 1.156 | 3.793 | 84.99 | 57.12 |
0.1620 | 4.115 | 6 | 13.296 | 26240 | 786 | 118000 | 10.50 | 0.309 | 1.317 | 4.321 | 74.59 | 50.13 |
0.1549 | 3.934 | 6 | 12.155 | 23989 | 814 | 122000 | 9.89 | 0.295 | 1.441 | 4.728 | 68.19 | 45.83 |
0.1443 | 3,665 | 7 | 10.549 | 20820 | 841 | 126000 | 8.87 | 0.275 | 1.660 | 5.446 | 59.18 | 39.77 |
0.1369 | 3.477 | 7 | 9.495 | 18739 | 869 | 128000 | 8.25 | 0.261 | 1.845 | 6.053 | 53.27 | 35.80 |
0.1285 | 3.264 | 8 | 8.366 | 16510 | 883 | 128000 | 7.38 | 0.245 | 2.094 | 6.870 | 46.95 | 31.55 |
0.1144 | 2.906 | 9 | 6.633 | 13090 | 883 | 128000 | 5.85 | 0.218 | 2.642 | 8.668 | 37.20 | 25.00 |
0.1019 | 2.588 | 10 | 5.260 | 10380 | 883 | 128000 | 4.47 | 0.194 | 3.329 | 10.922 | 29.52 | 19.84 |
0.0907 | 2.304 | 11 | 4.170 | 8230 | 883 | 128000 | 3.68 | 0.173 | 4.203 | 13.79 | 23.38 | 15.71 |
0.0808 | 2.052 | 12 | 3.309 | 6530 | 883 | 128000 | 2.92 | 0.154 | 5.295 | 17.373 | 18.57 | 12.48 |
Address:
Shijiawan Industrial Estate, Guxian Town, Yanshi City, Luoyang, Henan, China
Business Type:
Manufacturer/Factory, Trading Company
Business Range:
Electrical & Electronics
Management System Certification:
ISO 9001, ISO 14001
Company Introduction:
Huatong Cable Inc. has made outstanding contribution to STATE GRID, China SOUTH POWER GRID and the construction of domestic and foreign power market since foundation in 1993. The honors should be attributed to more than 20 years of constant R&D, market service and strong will.
Huatong Cable Inc. has set up overhead conductor division, power cable division and division of wire and cable for equipment. The division respectively takes charge of manufacture and marketing of overhead conductor, power cable and wire and cable for equipment. In 2002, our company set up the cable industry design and technology R&D department, providing technical support for product design and production. Our company makes independent innovation, and seeks cooperation with academic institutions including Shanghai Electric Cable Research Institute and China Electric Power Research Institute so as to meet the customized demands of customers and production needs of special cable. Now our company owns 25 exclusive rights to use trademark registered at home and abroad and 14 independent intellectual property patents. ACSR-720/50 aluminum cable steel reinforced has passed the technical appraisal of China Electricity Council. 500KV or above extra-high voltage conductor was put into production, came into service and had good operation record.
In 2013, Huatong Brand was awarded WELL KNOWN MARK OF China by the Trademark Office of the State Administration of Industry and Commerce, enjoying a high reputation in domestic market. The honor and legal status reflect the recognition of customers and support of the State Administration of Industry and Commerce. It is the only enterprise in cable industry in Henan that was awarded WELL KNOWN MARK OF China and Huatong brand will serve the society in the future.